GaN基低色温高显色白光LED

采用440nm短波长InGaN/GaN基蓝光LED芯片激发高效红、绿荧光粉制得高显色性白光LFD,研究了不同胶粉配比对LED发光性能的影响,结果表明,A胶、B胶、绿粉、红粉比重在0.5∶0.5∶0.2∶0.03时,在440 m蓝光激发下呈现了有两个谱带组成的发光光谱,分别是峰值为535 nm的特征光谱和643nm的特征光谱,胶粉通过均匀调配后能够有效的进行混光产生低色温白光,实验中最低色温可达3 251K,显色指数高达88.8,这比传统蓝光激发YAG荧光粉制得的白光LED色温更低,显色指数提高了26%.

GaN-based white-light-emitting diodes with low color temperature and high color rendering index

The luminescence properties of high color rendering white LED depending on the proportions of mixed phosphor powders were investigated by adopting green and red phosphors stimulated by a 440 nm InGaN/GaN based blue LED. The results show that when the proportion of A/B type silica gels and green/red phosphor powders is 0.5 : 0.5 : 0.2 : 0.03, two luminance bands are stimulated and their wavelength peaks are 535 and 643 nm, respectively. The minimum color temperature can reach 3 251 K, while the color rendering is as high as 88. 8. Compared with the traditional white LED fabricated by yellow YAG-phosphors-coated high efficiency 460 nm blue LED, the color temperature is lower and the color rendering index can be increased by almost 26%.