Modeling and simulation of long-wave infrared InAs/GaSb strained layer superlattice photodiodes with different passivants

Current–voltage characteristics of long-wave infrared (LWIR) InAs/GaSb strained layer superlattice photodiodes (cut-off wavelength ∼10 μm), passivated with different surface passivants, have been modeled and simulated using ATLAS software from SILVACO. The simulated results are fitted to previous experimental results obtained on unpassivated devices and those passivated by silicon-dioxide (SiO₂), silicon nitride (Si_xN_y) and zinc sulfide (ZnS). Surface parameters in terms of surface recombination velocity, shunt resistance and interface trap density are extracted for different passivants. The performance of silicon-dioxide passivated diode is solely dominated by a shunt leakage path with a shunt resistance value of 0.56 Ω-cm². Extracted electron and hole surface recombination velocities have values of 10⁵ cm/s and 10⁷ cm/s for unpassivated, 10³ cm/s and 10⁵ cm/s for Si_xN_y passivated and 10² cm/s and 10³ cm/s for ZnS passivated devices. Interface trap density follows a similar trend with values of 10¹⁵ cm⁻², 8.5 × 10¹⁴ cm⁻² and 10¹⁰ cm⁻² for unpassivated, Si_xN_y passivated and ZnS passivated devices respectively. The suitability and limitations of the simulation tool are discussed.