The luminescent properties of CaYBO4:Ln(Ln=Eu, Tb) under UV-VUV range

The luminescent properties of CaYBO₄:Ln(Ln=Eu³⁺, Tb³⁺) were investigated under ultraviolet (UV) and vacuum ultraviolet (VUV) region. The CT band of Eu³⁺ at about 245 nm blue-shifted to 230 nm in VUV excitation spectrum; the band with the maximum at 183 nm was considered as the host lattice absorption. For the sample of CaYBO₄:0.08Tb³⁺, the bands at about 235 and 263 nm were assigned to the f-d transitions of Tb³⁺ and the CT band of Tb³⁺ was calculated according to Jφrgensen's theory. Under UV and VUV excitation, the main emission of Eu³⁺ corresponding to the ⁵D₀-⁷F₂ transition located at about 610 nm and two intense emission of Tb³⁺ from the ⁵D₄-⁷F₅ transition had been observed at about 542 and 552 nm, respectively. With the incorporation of Gd³⁺ into the host lattice of CaYBO₄, the luminescence of Tb³⁺ was enhanced while that of Eu³⁺ was decreased because of their different excitation mechanism.