Electrical conductivity and local structure of lithium tin iron vanadate glass

A relationship between electrical conductivity (σ) and local structure of 15Li₂O·10Fe₂O₃·xSnO₂·(70–x)V₂O₅·5P₂O₅ glass (x = 0–20 mol%), abbreviated as xLFSVP glass, was investigated by ⁵⁷Fe- and ¹¹⁹Sn-Mössbauer spectroscopies, differential thermal analysis (DTA) and dc-four probe method. A small increase in quadrupole splitting (Δ) for Fe^III was observed from 0.70 to 0.74_{± 0.02} mm s^???1 with an increase of “x”, whereas isomer shift (Δ) values of 0.40_±0.01 mm s^???1 were independent of “x”. This result suggests that local distortion of Fe^IIIO₄ tetrahedra was slightly increased in SnO₂-containing vanadate glasses, which was reflected as an increase in glass transition temperature (T_g) from 266 to 285_±5 °C. A slope of 675 K / (mm s^???1) obtained in ‘T_g vs. Δ plot’ proved that Fe^III occupied the site of network former (NWF). An isothermal annealing of 10LFSVP glass at 500 °C for 100 min resulted in a marked decrease of Δ from 0.72 to 0.56_±0.02 mm s^???1, indicating that local distortion of FeO₄ tetrahedra was reduced by the structural relaxation of 3D-network. In contrast, identical δ and Δ values of 0.07_±0.01 and 0.53_±0.02 mms^???1, respectively, were observed in ¹¹⁹Sn-Mössbauer spectra of 10LFSVP glass before and after the annealing. These results indicate that Sn^IVO₆ octahedra are loosely bound in the glass matrix as a network modifier (NWM). A marked increase in σ from 7.4 × 10^???7 to 9.1 × 10^???3 S cm^???1 was observed in 20LFSVP glass after the isothermal annealing, indicating that structural relaxation of 3D-network evidently causes a marked increase in σ.