Verbindungen A3M5 (A = Erdalkalimetall,M = Triel/Tetrel): Eine Fallstudie zur strukturellen und elektronischen Stabilität polarer intermetallischer Phasen

Compounds A₃M₅ (A = alkaline earth, M = triel/tetrel): A Case Study on Structural and Electronic Factors Stabilizing Polar Intermetallics Starting from the non electron precise binary compounds Ca₃Ga₅/Sr₃In₅ (Hf₃Ni₂Si₃ type) and Ba₃Al₅ at one hand and Ba₃Pb₅ (Pu₃Pd₅ type) at the other hand, a series of new ternary intermetallics of the general formula A₃M₅ (A: alkaline earth, M: triel/tetrel) has been synthesized, structurally characterized and studied by band structure calculations. The chemical substitution of M in A₃M₅ allows, via the continous variation of the radius ratio (r_A:r_M) and the valence electron number (VE/M) the detection of the geometrically and electronically determined stability ranges of the three structure types formed by the binary compounds. At values of r_A:r_M between 1.30 and 1.52 in the triel rich region of A₃M′_xM″_5?x the Hf₃Ni₂Si₃ type (orthorhombic, space group Cmcm) is formed: In Ca₃Ga₅ up to 1.8 Ga can be substituted by Al, in Sr₃In₅ similar amount of In can be replaced by either Al or Ga. The mixed trielide Sr₃Al_2.6Ga_2.4 (a = 468.4(1), b = 1132.5(1), c = 1570.0(2) pm, R1 = 0.0261) can be obtained, although both corresponding binary phases are not known. At larger values of the ratio r_A/r_M as in Ba₃Al₃Ga₂ (Ba₃Al₅ type, hexagonal, space group P6₃/mmc, a = 598.9(1), c = 1456.0(3) pm, R1 = 0.0353) layers of condensed M₅ building blocks with Al‐Al partial bonds are formed. Substituting one In position in Sr₃In₅ against Pb results in the isotypic, but electron precise Zintl compound Sr₃In₄Pb (a = 506.1(1), b = 1191.8(3), c = 1650.2(4) pm, R1 = 0.0286), where the Fermi level in shifted into a distinct minimum of the density of states. Conversely, at the tetrele rich end of the series A₃In_xPb_5?x, characterized by compounds of the Pu₃Pd₅ type (orthorhombic, space group Cmcm) with almost isolated nido clusters M₅, a minimum of the DOS can be reached, if Pb is partially substituted by In (A₃In_xPb_5?x with A = Sr/Ba: x = 0.7/0.6; a = 1084.6(2)/1118.6(2), b = 867.1(2)/904.4(1), c = 1104.8(2)/1133.9(2) pm, R1 = 0.0394/0.0434).