Sol-gel polyimide-silica composite membrane: gas transport properties

The effect of introduction of silica particles prepared by the sol-gel technique on the gas transport properties of a polyimide film was studied. The sorption and permeation of N₂, O₂, CO₂, H₂ and CH₄ were studied and correlated with morphological changes in the polymer structure. From sorption isotherms, we observed that the composite membrane presents higher solubility coefficients than the polyimide one. The solubility coefficient ratio between the composite and the polyimide is about 1.5–2.0. The isotherms were analyzed in terms of the dual mode sorption. The Henry's coefficient and the Langmuir's affinity and saturation constants were obtained allowing to calculate the Langmuir to Henry concentration ratios as function of the gas pressure. These ratios decrease until zero within a certain pressure range as long as the Langmuir's mode is acting and they are higher for the polyimide membrane when compared with the composite one. This study was completed with calorimetric measurements during the sorption. The gas interaction energy in kJ/mol decreases within the same pressure range as previously described. The measured energies are higher for the polyimide film when compared with the composite one because the polyimide membrane presents a stronger energetic effect caused by a higher Langmuir's contribution. From permeation studies at 3.15⁵ Pa, the composite membrane showed higher permeability coefficients and permselectivities than the polyimide one. All these results were explained, taking into account the difference on the imidization degree of both membranes and the morphological changes which may be induced by the silica nodules in the organic/inorganic interphases.