Mixtures are expected to show anomalous behavior in their viscoelastic properties close to a critical point. In this study, the reheological behavior of blends of polystyrene and poly (vinyl methyl ether) below, close to, and above the phase separation temperature T_s was investigated. Rheological measurements were carried out at three different compositions in the melt. Below and far from T_s, a satisfactory superposition of the storage and loss moduli G' and G″ was observed at all temperatures and frequencies. Close to T_s deviations were observed for G' at low frequencies (the so-called terminal zone). Above T_s G″ values was still observed over the whole range of frequencies and temperatures. The deviations observed for G' near T_s can be interpreted as due to the presence of significant concentration fluctuations. Plots of log (G'/G″²) as a function of temperature were shown to be sensitive to this anomalous behavior.