Spectroscopic properties of RBiBO4 (R = Ca,Sr) glasses doped with TiO2

Transparent glasses, melt quenching derived, containing 10RO·20Bi₂O₃·(70 ? x)B₂O₃·xTiO₂ R = Ca, Sr] with x = 0, 0.5, 1.0 wt% were characterized by X-ray powder diffraction. Physical and spectroscopic properties viz., density, absorption, emission, electron paramagnetic resonance (EPR) and FTIR were investigated. The absorption band around 823 nm in pure glass samples is attributed to the electronic transition of ³P₀ to ³P₂ of Bi⁺ radicals. A small absorption hump centered around 609 nm is found in all doped glasses due to ²T_2g to ²E_g transition of octahedral Ti³⁺ ions. The emission results revealed that all the samples exhibit a broad emission band covering entire visible-light range, with λ_ex = 360 nm, centered 470–520 nm corresponds to electronic transition of ³P₁ to ¹S₀ of Bi³⁺ ions, therefore the present materials can be potentially used as tunable or full-color display systems. And a strong emission around 706 nm with λ_ex = 514 nm due to transition of ²P_3/2 to ²P_1/2 of Bi²⁺ ions. In SrO mixed glasses Ti⁴⁺ ions effect the environment of Bi³⁺ ion symmetry units from C₂ to C_3i. A small EPR signal (at room temperature) is observed in titanium doped glasses due to Ti³⁺ ions. In both the series with increase of TiO₂ concentration BO₄ units are gradually converted into BO₃ units and new cross linkages are formed, like B–O–Ti, Bi–O–Ti at the expense of B–O–B bonds.