Magnetoresistance of La0.67Sr0.33MnO3 epitaxial films grown on a substrate with low lattice mismatch

The structure, electrical resistivity, and magnetoresistance of La_0.67Sr_0.33MnO₃ heteroepitaxial films (120-nm thick) practically unstrained by lattice mismatch with the substrate were studied. A strong maximum of negative magnetoresistance of ≈27% (for μ₀H = 4 T) was observed at T ≈360 K. While the magnetoresistance decreased monotonically in magnitude with decreasing temperature, it was still in excess of 2% at 150 K. For T < 250 K, the temperature dependence of the electrical resistivity ρ of La_0.67Sr_0.33MnO₃ films is fitted well by the relation ρ = ρ₀ + ρ ₁(H)T^2.3, where ρ₀ = 1.1×10^?4 Ω cm, ρ₁(H = 0) = 1.8×10^?9 Ω cm/K^2.3, and ρ₁(μ₀H = 4 T)/ρ₁(H = 0) ≈0.96. The temperature dependence of a parameter γ characterizing the extent to which the electrical resistivity of the ferromagnetic phase of La_0.67Sr_0.33MnO₃ films is suppressed by a magnetic field (μ ₀H = 5 T) was determined.