Structural,Magnetic, and Electrical Properties of Al3+ Substituted CuZn-ferrites |
| |
Authors: | S M Ramay Saadat A Siddiqi S Atiq M S Awan S Riaz |
| |
Institution: | 1.Center of Excellence in Solid State Physics, University of the Punjab, Lahore-54590, Pakistan2.School of Science and Engineering, Lahore University of Management & Sciences (LUMS), Lahore 54972, Pakistan3.COMSATS Institute of Information Technology, Islamabad, Pakistan |
| |
Abstract: | Nanocrystalline Cu0.5Zn0.5Fe2-xAlxO2 (x=0.0, 0.1, 0.2, 0.3, 0.4, and 0.5) ferrite materials were synthesized using standard solid state reaction technique. The effects of Al3+ contents on the structural, electrical, and magnetic properties were investigated. Single phase cubic spinel structure was revealed by X-ray diffraction analysis. The crystallite size was evaluated considering the most intense diffraction peak (311) using Scherrer formula. Lattice constant decreased, whereas porosity increased with the increase in Al3+ concentration. The value of saturation magnetization decreased with increasing aluminum contents. Temperature dependent value of direct current electrical resistivity has been determined. It is observed that the substitution of Al3+ has significant impact on the dielectric constant, tangent of dielectric loss angle and dielectric loss factor. The variation in dielectric properties was attributed to space charge polarization. |
| |
Keywords: | Oxide material Ferrite Solid state reaction Electrical resistivity Dielectric constant |
|
| 点击此处可从《化学物理学报(中文版)》浏览原始摘要信息 |
| 点击此处可从《化学物理学报(中文版)》下载免费的PDF全文 |
|