Subsolidus phase equilibria and properties in the system Bi2O3:Mn2O3±x:Nb2O5

Subsolidus phase relations have been determined for the Bi-Mn-Nb-O system in air (750-900 °C). Phases containing Mn²⁺, Mn³⁺, and Mn⁴⁺ were all observed. Ternary compound formation was limited to pyrochlore (A₂B₂O₆O′), which formed a substantial solid solution region at Bi-deficient stoichiometries (relative to Bi₂(Mn,Nb)₂O₇) suggesting that ≈14-30% of the A-sites are occupied by Mn (likely Mn²⁺). X-ray powder diffraction data confirmed that all Bi-Mn-Nb-O pyrochlores form with structural displacements, as found for the analogous pyrochlores with Mn replaced by Zn, Fe, or Co. A structural refinement of the pyrochlore 0.4000:0.3000:0.3000 Bi₂O₃:Mn₂O_3±x:Nb₂O₅ using neutron powder diffraction data is reported with the A and O′ atoms displaced (0.36 and 0.33 Å, respectively) from ideal positions to 96g sites, and with Mn²⁺ on A-sites and Mn³⁺ on B-sites (Bi_1.6Mn²⁺_0.4(Mn³⁺_0.8Nb_1.2)O₇, (?227), a=10.478(1) Å); evidence of A or O′ vacancies was not found. The displacive disorder is crystallographically analogous to that reported for Bi_1.5Zn_0.92Nb_1.5O_6.92, which has a similar concentration of small B-type ions on the A-sites. EELS spectra for this pyrochlore were consistent with an Mn oxidation between 2+ and 3+. Bi-Mn-Nb-O pyrochlores exhibited overall paramagnetic behavior with negative Curie-Weiss temperature intercepts, slight superparamagnetic effects, and depressed observed moments compared to high-spin, spin-only values. At 300 K and 1 MHz the relative dielectric permittivity of Bi_1.600Mn_1.200Nb_1.200O₇ was ≈128 with tan δ=0.05; however, at lower frequencies the sample was conductive which is consistent with the presence of mixed-valent Mn. Low-temperature dielectric relaxation such as that observed for Bi_1.5Zn_0.92Nb_1.5O_6.92 and other bismuth-based pyrochlores was not observed. Bi-Mn-Nb-O pyrochlores were readily obtained as single crystals and also as textured thin films using pulsed laser deposition.