Swelling effect onα-relaxation in high density polyethylene

Summary Swelling effects of carbon tetrachloride on the mechanical relaxations in the crystal mat and the melt-crystallized samples of high density polyethylene were studied using a torsion pendulum. A very strong-relaxation peak appears by swelling at the low temperature side of the original-relaxation for the crystal mat. It was shown that this strong-relaxation originates from the slippage between the highly swollen lamellae. For the melt-crystallized sample, the-relaxation peak is decreased by swelling, but its temperature is unchanged. This behavior suggests that the-relaxation in the melt-crystallized sample originates mainly from deformation process of intermosaic block region. The swelling effect on-relaxation was also discussed.

---

Zusammenfassung Quellungseffekte von Tetrachlorkohlenstoff auf das mechanische Relaxationsverhalten in Einkristall-Matten und schmelzkristallisierten Proben von linearem Polyäthylen wurden mit den Torsionspendeln untersucht. Ein sehr starkes-Maximum tritt durch die Quellung bei tieferen Temperaturen als der der-Relaxation in den nicht gequollenen Einkristall-Matten auf. Es wird gezeigt, daß diese starke-Relaxation auf das Gleiten der ausreichend gequollenen Lamellen zurückzuführen ist. Bei schmelzkristallisierten Proben wird das-Maximum durch die Quellung erniedrigt, seine Temperaturlage wird jedoch nicht verändert. Dies zeigt, daß die-Relaxation in der schmelzkristallisierten Probe hauptsäcblich auf Deformations-Prozessen in den Blöcken beruht. Auch die Quellungseffekte auf die-Relaxationen wurden diskutiert.