Double‐frequency properties of In:LiNbO3 crystals

1 mol%, 2 mol%, 3 mol%, 4 mol% and 5 mol% In³⁺ doped LiNbO₃ crystals were grown by the Czochralski method, respectively. Oxidized treatment of some crystals was carried out. The infrared transmission spectra and photo‐damage resistance of the samples were measured. The results showed that the OH^‐ absorption peaks of In(3mol%):LiNbO₃, In(4mol%):LiNbO₃ and In(5mol%):LiNbO₃ crystals were located at about 3508 cm^‐1, while those of In(1mol%):LiNbO₃ and In(2mol%):LiNbO₃ crystals were located at about 3484cm^‐1. When the doped In³⁺ concentration reached its threshold in LiNbO₃ crystal, photo‐damage resistance of In:LiNbO₃ crystals was two orders of magnitude higher than that of pure LiNbO₃ crystal. The experimental results of the second harmonic generation (SHG) showed that the phase matching temperatures of In:LiNbO₃ crystals were lower than those of Zn:LiNbO₃ and Mg:LiNbO₃ crystals and the SHG efficiency reached 38%. Oxidization treatment was also found to make the dark trace resistance of crystals increase. (© 2005 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)