| Abstract: | A high‐tension annealing (HTA) method has been applied to zone‐annealed poly(ethylene‐2,6‐naphthalate) (PEN) fibers in order to further improve their mechanical properties. The HTA treatment was carried out under an applied tension of 428 MPa at a treating temperature of 175 °C. The applied tension was close to the tensile strength at 175 °C. The resulting HTA fiber had a birefringence of 0.492 and degree of crystallinity of 57%. Wide‐angle X‐ray diffraction (WAXD) photographs of the HTA fibers showed three reflections (010, 100, and 1 10) attributed to an α form crystal, but no (020) reflection attributed to a β form was observed in the equator. The tensile modulus and tensile strength increased with processing, and the HTA fiber had a maximum modulus of 33 GPa, a tensile strength of 1.1 GPa, and a storage modulus of 33 GPa at 25 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 61–67, 2000 |