5 μm thick 3C-SiC layers grown on Ge-modified Si(100) substrates

The effect of the germanium coverage prior to the epitaxial growth of 5 μm thick 3C-SiC on Si(100) substrates were evaluated with Atomic Force Microscopy and μ-Raman spectroscopy. The 3C-SiC layers were grown by atmospheric pressure chemical vapor deposition via a special procedure leading to layers with compressive instead of tensile stress. The Ge amount was varied from 0 up to 2 ML. The obtained results showed that the residual stress inside the layers is shifted in the compressive direction; the crystalline quality is improved with the Ge introduction but on the account of the surface roughness. These results open the route for the use of Ge-modified Si(100) as a potential substrate in order to improve the heteroepitaxial growth of 3C-SiC on silicon substrates.