Investigation of the quasi-ternary system LaMnO3-LaCoO3-“LaCuO3”—I: the series La(Mn0.5Co0.5)1−xCuxO3−δ

The La(Mn_0.5Co_0.5)_1−xCu_xO_3−δ series with x=0, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8 and 1 was synthesized by the Pechini method to obtain insight into the phase formation in the quasi-ternary LaMnO₃-LaCoO₃-“LaCuO₃” system caused by the instability of LaCuO₃ under ambient conditions. After sintering at 1100°C some remarkable results were obtained: LaMn_0.3Co_0.3Cu_0.4O_3−δ crystallized as a single phase in the orthorhombic perovskite structure typical of LaCuO₃. Among the synthesized compositions this compound showed the highest electrical conductivity in air at 800°C (155 S cm⁻¹) and also the highest thermal expansion coefficient (α_30−800°C=15.4×10⁻⁶ K⁻¹). The LaCuO_3−δ composition also crystallized as a single phase but in a monoclinic structure although previous investigations have shown that other phases are preferably formed after sintering at 1100°C. The electrical conductivity and thermal expansion coefficient were the lowest within the series of compositions, i.e. 9.4 S cm⁻¹ and 11.9×10⁻⁶ K⁻¹, respectively.