Visible luminescence of Al2O3 nanoparticles embedded in silica glass host matrix |
| |
| Authors: | L El Mir A Amlouk |
| |
| Institution: | a Laboratoire de Physique des Matériaux et des Nanomatériaux Appliquée à l’Environnement, Faculté des Sciences de Gabès, Cité Erriadh Manara Zrig, 6072 Gabès, Tunisie
b Institut des NanoSciences de Paris (INSP), UMR CNRS 7588, Universités Pierre et Marie Curie (Paris 6) et Denis Diderot (Paris 7), Campus Boucicaut, 140 rue de Lourmel, F-75015 Paris, France |
| |
| Abstract: | This paper deals with the sol-gel elaboration and defects photoluminescence (PL) examination of Al2O3 nanocrystallites (size ∼30 nm) confined in glass based on silica aerogel. Aluminium oxide aerogels were synthesized using esterification reaction for hydrolysis of the precursor and supercritical conditions of ethyl alcohol for drying. The obtained nanopowder was incorporated in SiO2 host matrix. After heating under natural atmosphere at 1150 °C for 2 h, the composite Al2O3/SiO2 (AS) exhibited a strong PL bands at 400-600 and 700-900 nm in 78-300 K temperature range. PL excitation (PLE) measurements show different origins of the emission. It was suggested that OH-related radiative centres and non-bridging oxygen hole centres (NBOHCs) were responsible for the bands at 400-600 and 700-900 nm, respectively. |
| |
| Keywords: | A Nanostrutures A Optical materials A Interfaces B Crystal growth B Sol-gel growth |