Drawing of poly(p-phenylene sulfide) by solid-state coextrusion

The effects of drawing temperature on the physical and mechanical properties of poly(p-phenylene sulfide) have been studied. A melt-quenched film was drawn by solid-state coextrusion both below (75°C) and above (95 and 110°C) the glass transition temperature T_g (85°C) of PPS. The maximum extrusion draw ratio (EDR_max) increased from 3.4 to 5.6 with increasing extrusion temperature T_e from 75 to 110°C. It was found that extrusion drawing just above the T_g of PPS (95°C) produced more stress-induced crystals. A high efficiency of draw in the amorphous region was achieved by extrusion at T_e-75°C. The tensile modulus at EDR_max decreased from 5.1 to 3.5 GPa with increasing T_e from 75 to 110°C. The low efficiency of draw for the samples extruded at 110°C is explained in terms of disentanglement and chain slippage during drawing due to a less effective network.