Bridgman growth and properties of potassium lithium niobate single crystals

Transparent KLN crystals 10mm in diameter and 25 to 45mm in length have been grown by the modified vertical Bridgman technique from different melts in the range of 3035mol% K₂O, 1723mol% Li₂O and 4350mol% Nb₂O₅. The growth conditions are a growth rate of less than 0.25 mm/hr, temperature gradient in solid-liquid interface of 23 °C/mm and growth direction of <110>. As-grown KLN crystals have tetragonal tungsten bronze structure. Most of the as-grown crystals do not crack when cooling through the paraelectric/ferroelectric phase transition. 180° domain structures are observed after the KLN crystal was etched in boiling 2HNO₃:Hf. Dielectric properties and transmission spectrum of the as-grown KLN crystals are measured.