Synthesis and properties of poly(ether imide)s based on the bis(ether anhydride)s from hydroquinone and its derivatives

Four bis(ether anhydride)s, 4,4′‐(1,4‐phenylenedioxy)diphthalic anhydride (IV), 4,4′‐(2,5‐tolylenedioxy)‐diphthalic anhydride (Me‐IV), 4,4′‐(2‐chloro‐1,4‐phenylenedioxy)diphthalic anhydride (Cl‐IV), and 4,4′‐(2,5‐biphenylenedioxy)diphthalic anhydride (Ph‐IV), were prepared in three steps starting from the nucleophilic nitrodisplacement reaction of 4‐nitrophthalonitrile with the potassium phenoxides of hydroquinone and various substituted hydroquinones such as methylhydroquinone, chlorohydroquinone, and phenylhydroquinone in N,N‐dimethylformamide, followed by alkaline hydrolysis and dehydration. Four series of poly(ether imide)s were prepared from bis(ether anhydride)s with various aromatic diamines by a classical two‐step procedure. The inherent viscosities of the intermediate poly(amic acid)s were in the range of 0.40–2.63 dL/g. Except for those derived from p‐phenylenediamine and benzidine, almost all the poly(amic acid)s could be solution‐cast and thermally converted into transparent, flexible, and tough polyimide films. Introduction of the chloro or phenyl substituent leads to a decreased crystallinity and an increased solubility of the polymers. The glass transition temperatures (T_g) of these polyimides were recorded in the range of 204–263°C. In general, the methyl‐ and chloro‐substituted polyimides exhibited relatively higher T_gs, whereas the phenyl‐substituted ones exhibited slightly lower T_gs compared to the corresponding nonsubstituted ones. Thermogravimetric analysis (TG) showed that 10% weight loss temperatures of all the polymers were above 500°C either in nitrogen or in air. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 665–675, 1999