The electron microscope characterization of the fine structure of nylon 6: II. On the rearrangement of the structure during cold-drawing

The transmission electron microscope (TEM) visualization of the supermolecular structure of cold-drawn, oriented nylon 6 bulk material (bristles) by stained ultra-thin sections is reported. For evaluating the electron micrographs optical diffraction (OD) has been applied in comparison with small angle X-ray scattering (SAXS). The deformation of the spherulites was followed by polarization microscopy. In addition, investigations were carried out on commercial nylon 6 fibres. As the main result a transverse structure was revealed within the drawn samples at draw ratios between =4 and 4.5, consisting of mosaic crystals which show some lateral alignment. The structure is described by a modified layer lattice model. While the long period may increase slightly during drawing, the crystallite thickness remains almost constant. Fibres with =3.4 show a similarly oriented structure though the lateral alignment of the crystals is not so pronounced.