Electrochemical behavior of methyl viologen at graphite electrodes modified with Nafion sol–gel composite

Electrodes were prepared by spin-coating spectroscopic graphite rods with a Nafion doped sol. Coating solutions consisting of Nafion:TEOS (tetraethoxysilane) ratios of 3:1 and 4:1 gave smooth films on the electrode surface. These modified electrodes were evaluated and compared with Nafion modified and bare spectroscopic graphite electrodes using methyl viologen (MV²⁺) as a representative cationic electroactive probe. Substantial partitioning of MV²⁺ into the Nafion:sol–gel matrix to the electrode surface was observed by cyclic voltammetry and square wave voltammetry. Cyclic voltammograms of MV²⁺ in 0.1 M NaCl at Nafion:sol–gel 4:1 modified electrodes showed a reversible reduction to MV⁺ with E^0′=?0.695 V vs. Ag/AgCl. Results of scan rate variation showed the wave to be characterized by semi-infinite diffusion for scan rates in the range 50–500 mV/s. Slowing the scan rate below 50 mV/s resulted in a transition to thin-layer behavior. MV²⁺ partitioned much more quickly into the sol–gel-Nafion modified electrodes compared to pure Nafion modified electrodes. Reversibility of the MV²⁺-loaded modified Nafion-doped sol–gel coatings on electrodes was obtained by soaking in 1 M NaCl solution. Concentration calibration plots for MV²⁺ at the sol–gel-Nafion modified electrodes were nonlinear. Substantial enhancement of current signal at low concentrations was observed by square wave voltammetry.