Simultaneously Enhancing Mechanical Properties and Melt Flow Ability of Polyamide 6 by Blending with a Hyperbranched Polymer

A series of polyamide 6/hyperbranched polymers (PA6/HBP) blends with different HBP contents was prepared by melt processing using a twin-screw extruder. The HBP was synthesized on the basis of pentaerythritol and dimethyl terephthalate according to a one-step method. The melt flow behavior, crystallization behavior, morphology, and mechanical properties of the PA6/HBP blends were investigated. The results showed that the melt flow index of the blends was greatly improved by a small amount of HBP. The yield strength, tensile modulus, Izod impact strength, and flexural strength of samples were simultaneously enhanced from 54.6 MPa, 0.5 GPa, 3.8 kJ/m², 56.9 MPa for pure PA6 to 61.1 MPa, 0.7 GPa, 5.3 kJ/m², 67.1 MPa for PA6 blends with 2.0 wt% HBP, respectively. The PA6/HBP blends showed the higher content of α-form crystal and a higher degree of crystallinity than those of pure PA6.