Preparation and characterization of mesoporous TiO2-CeO2 nanopowders respond to visible wavelength

Mesoporous TiO₂-CeO₂ nanopowders responding to visible wavelength were synthesized by using a surfactant assisted sol-gel technique. They were obtained using metal alkoxide precursors modified with acetylacetone (ACA) and laurylamine hydrochloride (LAHC) as surfactant. The samples were characterized by XRD, nitrogen adsorption isotherm, SEM, TEM, and selected area electron diffraction (SAED), respectively. The 95 mol% TiO₂-5 mol% CeO₂ system yielded single anatase phase, however, further addition of the CeO₂ formed cubic CeO₂ structure while anatase TiO₂ decreased. Additions of 5 and 10 mol% CeO₂ increased the surface area, but those of 25, 50, and 75 mol% CeO₂ did not affect it very much. By using this mixed metal oxides system, TiO₂ can be modified to respond to the visible wavelength. The mixed metal oxides had catalytic activity (evaluating the formation rate of I₃⁻) about 2-3 times higher than pure CeO₂, while nanosize anatase type TiO₂ materials had no catalytic activity under visible light. The catalytic activity was almost proportional to the specific surface area. The formation rate of I₃⁻ was much improved by changing the calcination temperature and calcination period. Highest catalytic activity in this study was obtained for the 50 mol% TiO₂-50 mol% CeO₂ nanopowders calcined at 250 °C for 24 h.