Body temperature-responsive gels derived from hydroxypropylcellulosebearing lignin II: adsorption and release behavior

The lower critical solution temperature (LCST) of hydroxypropylcellulose bearing lignin (HPC-L) prepared from unbleached pulp depends on the amount of residual lignin. An HPC-L gel having thermal properties reflective of original HPC-L was prepared using ethyleneglycol diglycidylether as a crosslinker, as previously reported [Uraki et al. (2004) Carbohydr. Polym. 58:123–130], and the volume transition temperature was detected as an endothermic peak by differential scanning calorimetry (DSC). The adsorption and release behavior of the guest molecules to/from this gel was then examined. When the adsorption of cationic and anionic guests was compared, cationic methylene blue (MB) was adsorbed in larger amounts than anionic methyl orange (MO). In addition, MB adsorption into the HPC-L gel was greater than MB adsorption into the HPC gel prepared from commercially available HPC. This suggests that residual lignin affects the adsorption of organic dyes. Significant differences were not observed with respect to the release of MB from HPC-L at 38 °C and lower temperatures. In the adsorption of surfactants, marked adsorption at around the critical micelle concentration of the ionic surfactants and gel swelling were observed. Such swelling did not occur in the aqueous nonionic surfactant solution, although the nonionic surfactant was adsorbed into the gel. Gel swelling may have been caused by the electrostatic repulsion of the ionic surfactants adsorbed onto the polymer chains within the gel structure.