Preparation and Properties of Highly Oriented Sr0.3Ba0.7Nb2O6 Thin Films by a Sol-Gel Process

We succeeded in the preparation of epitaxial or highly oriented strontium-barium niobate (Sr_0.3Ba_0.7Nb₂O₆) thin film by a sol-gel process. A homogeneous coating solution was prepared with Sr and Ba acetates and Nb(OEt)₅ as raw materials, and acetic acid and diethylene glycol monomethyl ether as solvents. Sr_0.3Ba_0.7Nb₂O₆ film sintered at 900°C on MgO(1 0 0) was oriented with c-axis perpendicular to the substrate surface. Sr_0.3Ba_0.7Nb₂O₆ film sintered at 700°C on SrTiO₃(1 0 0) was an epitaxial and oriented with c-axis in parallel to the substrate surface. Transmittance of Sr_0.3Ba_0.7Nb₂O₆ film (film thickness: 144 nm) was more than 60% at the range from 400 to 800 nm. Refractive index was 2.33 at 633 nm. Dielectric constant and dielectric loss of the Sr_0.3Ba_0.7Nb₂O₆ thin films prepared on polycrystal Pt substrates were 600 and 0.06 at room temperature and 1 kHz, respectively. The curie temperature (T_c) of polycrystalline Sr_0.3Ba_0.7Nb₂O₆ thin films was about 200°C. At room temperature and 50 kHz, remanent polarization (P_r) and coercive field (E_c) of the polycrystalline thin films were 1.79 C/cm² and 2.69 kV/cm, respectively.