Effect of carbon coating process on the structure and electrochemical performance of LiNi0.5Mn0.5O2 used as cathode in Li-ion batteries

LiNi_0.5Mn_0.5O₂ powder was synthesized by a coprecipitation method. LiOH.H₂O and coprecipitated [(Ni_0.5Mn_0.5)C₂O₄] precursors were mixed carefully together and then calcined at 900°C. Surface modified cathode materials were obtained by coating LiNi_0.5Mn_0.5O₂ with a thin layer of amorphous carbon using table sugar and starch as carbon source. Both parent and carbon-coated samples have the characteristic layered structure of LiNi_0.5Mn_0.5O₂ as estimated from X-ray diffractometry measurements. Transmission electron microscope showed the presence of C layer around the prepared particles. TGA analysis emphasized and confirmed the presence of C coating around LiNi_0.5Mn_0.5O₂. It is obvious that the carbon coating appears to be beneficial for the electrochemical performance of the LiNi_0.5Mn_0.5O₂. A capacity of about 150 mAh/g is delivered in the voltage range 2.5–4.5 V at current density C/15 for carbon coated LiNi_0.5Mn_0.5O₂ in comparison with about 165 mAh/g obtained for carbon free LiNi_0.5Mn_0.5O₂ at the same current density and voltage window. About 92% and 82% capacity retention was obtained at 50th cycle for coated LiNi_0.5Mn_0.5O₂ using sucrose and starch, respectively; whereas, 75% was retained after only 30th cycle for carbon free LiNi_0.5Mn_0.5O₂. This improvement is mainly attributed to the presence of thin layer of carbon layer that encapsulate the nanoparticles and improve the conductivity and the electrochemical performance of LiNi_0.5Mn_0.5O₂.