Effect of α-methylstyrene of the curing behaviour of vinyl ester resins |
| |
Authors: | R Bhatnagar I K Varma |
| |
Institution: | (1) Centre for Materials Science and Technology, Indian Institute of Technology, Hauz Khas, 110016 New Delhi, India |
| |
Abstract: | The curing behaviour of bismethacryloxy derivative of diglycidyl ether of bisphenol A (vinyl ester resin) containing styrene as the reactive diluent (40% w/w) was studied using gel point determination method and DSC. Seven samples of styrene/-methylstyrene in the ratio 400, 355, 3010, 2515, 2020, 1525 and 040 were studied. Delayed curing was observed in samples containing increasing proportions of -methylstyrene. The energy of activation decreased from 869 kJ mol–1 to 333 kJ mol–1 as the concentration of -methylstyrene increased in the formulations. However, no difference in thermal stability was observed by replacement of styrene by -methylstyrene. It was concluded that in vinyl ester resin samples 10–15% -methylstyrene and 30-25% styrene can be used as reactive diluent.
Zusammenfassung Mittels DSC und Bestimmung der Gelierungstemperatur wurde das Aushärteverhalften des Bismethakryloxyderivaten des Diglycidyläthers von Bisphenol A (Vinylesterharz) mit 40 Gewichtsprozenten Styrol als reaktives Streckmittel untersucht. Es würden sieben Proben mit einem Styrol/-Methylstyrol Verhältnis von 400, 355, 3010, 2515, 2020, 1525 und 040 untersucht. Mit steigendem Anteil an -Methylstyrol konnte eine Verzögerung der Aushärtung sowie ein Absinken der Aktivierungsenergie von 869 kJ · mol–1 auf 333 kJ · mol–1 beobachtet werden. Der Ersatz von Styrol durch -Methylstyrol veränderte jedoch die thermische Stabilität in keiner Weise. Vinylesterharzproben mit 10–15% -Methylstyrol und 30–25% Styrol können als reaktive Streckmittel in Vinylesterharzen verwendet werden.
- - , 40 .% . /-, 400, 355, 3010, 2515, 2020, 1525 040. - . - 869 333 · –1. , .. , , 10–15% - 30–25% . |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|