Fabrication of NiO coated SiO2 and SiO2 coated NiO for the removal of Pb2+ ions |
| |
作者姓名: | Saba Noor Muhammad Waseem Umer Rashid Muhammad Anis-ur-Rehman Wajid Rehman Khalid Mahmood |
| |
作者单位: | a Department of Chemistry, Hazara University, Mansehra 21300, Pakistan;
b Department of Physics, COMSATS Institute of Information Technology, Islamabad 44000, Pakistan |
| |
摘 要: | We have prepared silica,SiO2coated NiO and NiO coated SiO2by sol-gel method.The physicochemical properties of the desired materials were investigated by surface charge properties,scanning electron microscopy(SEM),energy dispersive X-ray(EDX) spectroscopy,surface area measurements and X-ray diffraction(XRD) analyses.The point of zero charge(PZC) of the solid was determined by the salt addition method.In coated materials,two PZC values were noted representing the surface charge of their counterparts.The SEM image of SiO2coated NiO displays a uniform coating of silica on the surface of NiO whereas in case of NiO coated SiO2,a honeycomb like appearance was observed with highly porous structures.In the diffractograms of NiO,the characteristic peaks were suppressed in NiO coated silica however,no diffraction peak could be seen in SiO2coated NiO.Batch adsorption technique was applied for the removal of Pb2+ions from aqueous solution.The sorption trend for Pb2+ions was observed in the order of NiO coated SiO2〉 SiO2coated NiO 〉 NiO 〉 SiO2.This trend confirms that the coated materials have more sorption capacities than their parent counterparts.
|
关 键 词: | Characterization Coated materials Lead removal Sol–gel |
收稿时间: | 29 July 2013 |