Defect Structure and Up-conversion Luminescence Properties of ZrO2:Yb3+,Er3+ Nanomaterials

The up-converting ZrO₂:Yb³⁺,Er³⁺ nanomaterials were prepared with the combustion and sol–gel methods. FT-IR spectroscopy was used for analyzing the impurities. The crystal structures were characterized with X-ray powder diffraction and the mean crystallite sizes were estimated with the Scherrer formula. Up-conversion luminescence measurements were made at room temperature with IR-laser excitation at 977 nm. The IR spectra revealed the conventional and OH⁻ impurities for the combustion synthesis products. The structure of the ZrO₂:Yb³⁺, Er³⁺ nanomaterials was cubic except for the minor monoclinic and tetragonal impurities obtained with the sol–gel method. The materials showed red (650–700 nm) and green (520–560 nm) up-conversion luminescence due to the ⁴F_9/2→⁴I_15/2 and (²H_11/2, ⁴S_3/2)→⁴I_15/2 transitions of Er³⁺, respectively. The products obtained with the combustion synthesis exhibited the most intense luminescence intensity and showed considerable afterglow.