Structure and ferro-/piezoelectric properties of bimorph-shape CaBi4Ti4O15 films on Pt foils |
| |
| Authors: | K Kato K Tanaka K Suzuki T Kimura K Nishizawa T Miki |
| |
| Institution: | (1) National Institute of Advanced Industrial Science and Technology, 2266-98 Anagahora, Shimoshidami, Moriyama-ku, Nagoya 463-8560, Japan;(2) Nagoya Institute of Technology, Gokiso, Showa-ku, Nagoya 466-8555, Japan |
| |
| Abstract: | In-plane c-axis oriented CaBi4Ti4O15 (CBTi144) films were fabricated on Pt foils using a complex metal alkoxide solution. The a/b-axis orientation of the ferroelectric films was affected by the preferred orientation of Pt foil, which is associated with the thickness. The 500 nm-thick CBTi144 films showed good ferro- and piezoelectric properties on 0.010 mm-thick Pt foils. The Pr and Ec were 26  C/cm2 and 230 kV/cm, respectively, at an applied voltage of 75 V. The d33 was characterized as 25–34 pm/V by piezoresponse force microscopy. The values enhanced compared to those of the CBTi144 thin film with random orientation. The polar-axis oriented CBTi144 films would open for novel devices as Pb-free piezoelectric materials. PACS 77.84.-s; 68.37.-d; 81.15.-z |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|