Spin-glass-like behaviour and magnetic order in Mn[Cr0.5Ga1.5]S4 spinels

Magnetization and susceptibility were investigated as a function of temperature and magnetic field in polycrystalline MnCr_0.5Ga_1.5]S₄ spinel. The dc susceptibility measurements at 919 Oe showed a disordered ferrimagnetic behaviour with a Curie-Weiss temperature θ_CW=−55 K and an effective magnetic moment of 5.96 μ_B close to the spin-only value of 6.52 μ_B for Cr³⁺ and Mn²⁺ ions in the 3d³ and 3d⁵ configurations, respectively. The magnetization measured at 100 Oe revealed the multiple magnetic transitions with a sharp maximum at the Néel temperature T_N=3.9 K, a minimum at the Yafet-Kittel temperature T_YK=5 K, a broad maximum at the freezing temperature T_f=7.9 K, and an inflection point at the Curie temperature T_C=48 K indicating a transition to paramagnetic phase. A large splitting between the zero-field-cooled (ZFC) and field-cooled (FC) magnetizations at a temperature smaller than T_C suggests the presence of spin-glass-like behaviour. This behaviour is considered in a framework of competing interactions between the antiferromagnetic ordering of the A(Mn) sublattice and the ferromagnetic ordering of the B(Cr) sublattice.