Neutron irradiation effects on martensitic iron-nickel alloys

Summary Iron-nickel alloys in the range from 29 to 32 wt.% Ni have been irradiated with an integral flux of 3·10¹⁸ n cm⁻² and then subjected to martensitic transformation. the resistivity, magnetoresistivity and Hall-effect measurements performed on the irradiated samples allow us to support the formation of iron-rich or nichel-rich ordered microstructures and additional α-phase from the supersaturated γ-matrix. The nickel content of the above-ordered region, is evaluated from the behaviour of the anomalous Hall effect in the irradiated specimens with different composition.

---

Riassunto Leghe di ferro-nichel, con contenuto in Ni variabile dal 29% al 32%, sono state irradiate con un fascio di neutroni avente flusso integrale di 3·10¹⁸ n cm⁻² a 80°C e sono state successivamente sottoposte a trasformazione martensitica mediante raffreddamento. Le misure di resistività, di magnetoresistenza e di effetto Hall compiute sui campioni irradiati consentono di fare l'ipotesi della presenza nella fase supersatura γ di microstrutture ordinate, ricche di Fe o di Ni, oltre ad una fase α addizionale. Dal comportamento dell'effetto Hall anomalo nei campioni irradiati si è valutato il contenuto di Ni presente nelle regioni ordinate.