Etude Des Propriétés Physico-Chimiques De ZnRb 4 (P 3 O 9 ) 2 ·6H 2 O

The dehydration of ZnRb 4 (P 3 O 9 ) 2 ·;6H 2 O was investigated, between 25 and 600°;C, by TG-DTA, X-ray diffraction, IR. It leads, between 300 and 500°;C, to a mixture of long chain polyphosphates RbPO 3 and ZnRb 2 (PO 3 ) 4 which stays stable until its melting point. The IR (1400-30 cm m 1 ) and Raman spectra (1400-100 cm m 1 ) of ZnRb 4 (P 3 O 9 ) 2 ·;6H 2 O are reported and assignments of fundamental modes proposed and compared with theoretical results obtained via the MNDO method for P 3 O 9 ring with C s symmetry. (La déshydratation, sous pression atmosphérique, du cyclotriphosphate ZnRb 4 (P 3 O 9 ) 2 ·;6H 2 O, a ét´;e effectuée, entre 25 and 600°;C, par spectrométrie IR, diffraction des rayons X, ATG et ATD. Elle conduit, entre 300 and 500°;C, au mélange de polyphosphates RbPO 3 et ZnRb 2 (PO 3 ) 4 qui reste stable jusqu'à la fusion. Les spectres vibrationnels IR (1400-30 cm m 1 ) et Raman (1400-100 cm m 1 ) du sel étudié ont été interprétés dans le domaine des vibrations de valence et de déformation du cycle P 3 O 9 et comparés avec les résultats des calculs théoriques par la méthode MNDO pour un cycle isolé de symétrie C s .)