Amethyst and morion quartz gemstone raw materials from Turkey: color saturation and enhancement by gamma,neutron and beta irradiation

Color-enhancement investigations without using heating treatment from dull or pale to ideal saturation and/or changes to the formation of the rarer attractive colors are widely conducted to revalue abandoned gem material sources in the world. Such an investigation is carried out on pale or dull purple-colored amethyst and smoky-colored morion samples, which are two important gem species of the crystalline quartz (SiO₂) mineral that are currently abandoned in natural deposits in Turkey because of their unattractive coloration. The results of color enhancements observed on these samples, after irradiation with artificial gamma, neutron and beta beams, were examined by comparing with samples with the ideal color saturation and also with colorless samples, using optical absorption (OA) and radioluminescence (RL) spectroscopy. The ICP-AES analyses reveal that the main impurity elements of over 100 ppm in abundance in these quartz species are aluminum, iron and titanium for amethyst, and aluminum, iron, titanium and manganese for morion. The OA spectra indicate that vivid purple coloration of amethyst is due to the transmittance at about 395–420 nm band gap as a result of absorbance peaks at 375, 480 and 530 nm. These absorbances may be related to the unusual oxidized small proportions of certain impurity ions, after being exposed mainly to gamma irradiation, such as Al(IV) from the total aluminum, Ti(V) from the total titanium and Fe(IV) from the total iron, respectively. However, the RL spectroscopy of amethyst samples before and after they were exposed to artificial gamma, neutron and beta radiation beams demonstrates that the ions most affected by irradiation are Fe(IV) first and Al(IV) and Ti(V) second, and these ions represent the RL peaks at 600, 720 and 495 nm, respectively. The OA spectra indicate that dark smoky coloration in morion is due to a lack of transmittance at the visible region as a result of the absorbance peaks at 375, 450–490, 620 and 730 nm. These absorbances also may be related to the unusual oxidized small proportions of certain impurity ions by irradiation, such as Al(IV) from the total aluminum, Ti(V) from the total titanium and Mn(III) from the total manganese, respectively. In addition, the buoyancies of these absorbance peaks in the visible region produce the color hues between light smoky and dark smoky colorations in morion samples. These oxidized ion states are more resistant and stable against environmental destructive conditions in comparison with amethyst. Thus, the dark smoky coloration of morion becomes dull or pale after relatively longer periods. But, the RL spectroscopy of morion before and after being exposed to gamma, neutron and beta irradiation beams demonstrates that the most induced ions from the irradiation are Mn(III) and Al(IV) first and Ti(V) second. These ions represent the RL peaks at about 400, 720 and about 500 nm, respectively.