A comparative study of ion-induced damages in C60 and C70 fullerenes

The stability of fullerenes (C₆₀ and C₇₀) under swift heavy ion irradiation is investigated. C₆₀ and C₇₀ thin films were irradiated with 120 MeV Ag ions at fluences from 1×10¹² to 3×10¹³ ions/cm². The damage cross-section and radius of damaged cylindrical zone were found to be higher for C₆₀ than C₇₀ as evaluated by Raman spectroscopy, which shows that the C₇₀ molecule is more stable under energetic ion impact. The higher damage cross-section of the C₆₀ molecule compared with that of the C₇₀ molecule is explained on the basis of thermal conductivity in the framework of the thermal spike model. The surface morphology of pristine C₆₀ and C₇₀ films is studied by atomic force microscopy. UV-visible absorption studies revealed that band gap for C₆₀ and C₇₀ fullerenes thin films decreases with increasing ion fluence. Resistivity of C₆₀ and C₇₀ thin films decreases with increasing ion fluence but the decrease is faster for C₆₀ than C₇₀, indicating higher damage in C₆₀. Irradiation at a fluence of 3×10¹³ ions/cm² results in complete damage of fullerenes (C₆₀ and C₇₀) into amorphous carbon.