1. Department of Innovative and Engineered Material, Tokyo Institute of Technology, 4259 Nagatsuta-cho, Midori-ku, Yokohama 226-8503, Japan;2. Department of Materials and Life Sciences, Sophia University, Chiyoda, Tokyo 102-8554, Japan
Abstract:
Epitaxial (La0.07Sr0.93)SnO3 LSSO] films were deposited on CaF2 substrates by pulse laser deposition. The (1 0 0)c orientation of LSSO films was observed only on (1 1 0)CaF2, whereas (1 1 0)c orientation was found on (1 1 1)CaF2 and (1 0 0)CaF2. (0 0 1) polar axis oriented tetragonal Pb(Zr0.35Ti0.65)O3 films were grown on the fabricated (1 0 0)cLSSO∥(1 1 0)CaF2 by pulsed metal organic chemical vapor deposition. The (0 0 1)Pb(Zr0.35Ti0.65)O3∥(1 0 0)cLSSO∥(1 1 0)CaF2 stack structure exhibited about 70% transparency with an adsorption edge of approximately 330 nm.