The dc magnetic field,temperature and film thickness dependence of microwave surface resistance of YBCO and DyBCO thin films

We investigated the dc magnetic field and temperature dependences of the microwave surface resistance (R_s) of YBa₂Cu₃O_y (YBCO) and DyBa₂Cu₃O_y (DyBCO) superconducting thin films. The YBCO and DyBCO thin films, each with a thickness of 300, 500, or 700 nm, were deposited on MgO (1 0 0) substrates by the thermal co-evaporation method. The R_s was measured using the dielectric resonator method. A dc magnetic field of up to 5.0 T was applied parallel to the c-axis of the superconducting thin films. The results showed that the R_s value had almost the same temperature dependence at various thicknesses in a zero-external field. The R_s of the YBCO and DyBCO thin films increased with the applied dc magnetic field. The DyBCO thin films showed weaker magnetic field dependence of R_s than the YBCO thin films. The R_s ratio (defined as R_s(5 T)/R_s(0 T)) linearly increased with the film thickness. These results show that pinning strength decreased with an increasing film thickness.