Electrical conductivity of Ag/Na ion-exchanged titanosilicate glasses

The Ag₂O–TiO₂–SiO₂ glasses were prepared by Ag⁺/Na⁺ ion-exchange method from Na₂O–TiO₂–SiO₂ glasses at 380–450 °C below their glass transition temperatures (T_g), and their electrical conductivities were investigated as functions of TiO₂ content and the ion-exchange ratio (Ag/(Ag+Na)). In a series of glasses 20R₂O·xTiO₂·(80−x)SiO₂ with x=10, 20, 30 and 40 in mol%, the electrical conductivities at 200 °C of the fully ion-exchanged glasses of R=Ag were in the order of 10⁻⁵ or 10⁻⁴ S cm⁻¹ and were 1 or 2 orders of magnitude higher than those of the initial glasses of R=Na. The glass of x=30 exhibited the highest increase of conductivity from 3.8×10⁻⁷ to 1.3×10⁻⁴ S cm⁻¹ at 200 °C by Ag⁺/Na⁺ ion exchange among them. When the ion-exchange ratio was changed in 20R₂O·30TiO₂·50SiO₂ system, the electrical conductivity at 200 °C exhibited a minimum value of 7.6×10⁻⁸ S cm⁻¹ around Ag/(Ag+Na)=0.3 and increased steeply in the region of Ag/(Ag+Na)=0.5–1.0. When the ion-exchange temperature was changed from 450 to 400 °C, the conductivity of the ion-exchanged glass of x=30 decreased. The infrared spectroscopy measurement revealed that the ion-exchange temperature of 450 °C induced a structural change in the glass of x=30. The T_g of the fully ion-exchanged glass of x=30 was 498 °C. It was suggested that the incorporated silver ions changed the average coordination number of titanium ions to form higher ion-conducting pathway and resulted in high conductivity in the titanosilicate glasses.