The structure and luminescence properties of a novel orange emitting phosphor Y3MnxAl5−2xSixO12

A series of phosphors with the composition Y₃Mn_xAl_5−2xSi_xO₁₂ (x=0, 0.05, 0.1, 0.15, 0.2, 0.3, 0.4, 0.5, 0.6) was prepared through solid state reactions. X-ray powder diffraction analysis of samples shows that when co-doping content does not exceed 16% of Al³⁺, equimolar co-doping of Mn²⁺ and Si⁴⁺ does not change the garnet structure of phosphors, but makes the interplanar distance to decrease a certain extent. However, if the co-doping content exceeds 16%, new phases will form in the samples. The excitation and emission spectra of samples show that Mn²⁺ in Y₃Mn_xAl_5−2xSi_xO₁₂ emits broadband orange light (peak wavelength varies from 586 to 593 nm). With an increment in co-doping content, the emission intensity of the phosphors increases when the value of x is lower than 0.1 while it decreases when it is higher than 0.1 and the emission peak moves to a longer wavelength.