| Abstract: | Mode I (GIC) and Mode II (GIIC) interlaminar fracture toughness of carbon-fiber/epoxy composites have been investigated as a function of the amount of short Kevlar-29 fiber (SKF) and/or Nylon-6 powder (N6P) between continuous fiber layers. GIIC increased with increasing crack length as a consequence of the presence of SKFs bridging in the wake of propagating crack. GIIC of SKF alone could reach the maximum at an intermediate amount of SKF. GIIC of SKF and N6P was lower than that of SKF alone because N6P prevented the orientation of SKF to out-of-plane. The extent of SKF's bridging phenomenon may be influenced by the amount and orientation of SKF. GIC showed no significant effect with SKF and uniform irrespective of crack length. Scanning electron microscopy after GIIC test showed that new surfaces were created by extensive fiber bridging, pull-out and fracture of SKF in random direction without any fixed pattern. © 1997 John Wiley & Sons, Ltd. |