X-ray diffraction, vibrational and photoluminescence studies of the self-organized quantum well crystal H3N(CH2)6NH3PbBr4

We have prepared new semiconductor H₃N(CH₂)₆NH₃PbBr₄ crystals which are self-assembled organic-inorganic hybrid materials. The grown crystals have been studied by X-ray diffraction, infrared absorption and Raman spectroscopy scattering. We found that the title compound, abbreviated 2C₆PbBr₄, crystallizes in a two-dimensional (2D) structure with a P2₁/a space group. In the inorganic semiconductor sub-lattice, the corner sharing PbBr₆ octahedra form infinite 2D chains. The organic C₆H₁₈N₂⁺ ions form the insulator barriers between the inorganic semiconductor layers. Such a packing leads to a self-assembled multiple quantum well structure. Raman and infrared spectra of the title compound were recorded in the 50-500 and 400-4000 cm⁻¹ frequency regions, respectively. The assignment of the observed Raman lines was performed by comparison with the homologous compounds. Transmission measurements on thin films of 2C₆PbBr₄, obtained by the spin coating method, revealed a strong absorption peak at 380 nm. Luminescence measurements showed an emission line at 402 nm associated with radiative recombinations of excitons confined within the PbBr₆ layers. The electron-hole binding energy is estimated at 180 meV.