Phase formation and thermal stability of the compounds in the Bi2O3-PbO system

The scientific interest for the Bi₂O₃-PbO system has increased due to the importance of the PbO in the high-T _c superconducting phase formation in the Bi₂O₃-SrO-CaO-CuO system. Also Bi₂O₃-PbO system contains compounds with some specific semiconductor and dielectric properties and Bi₂O₃-based solid solutions are well known as high oxygen ion conductors.Previously, several low melting defined compounds have been identified in the system: 6Bi₂O₃·PbO; 3Bi₂O₃·2PbO; 4Bi₂O₃·5PbO; 4Bi₂O₃·6PbO and Bi₂O₃·3PbO.This work deals with the phase formation and thermal stability of these compounds. Under non-isothermal conditions, in all mixtures regardless of the Bi₂O₃/PbO ratio, the compound 6Bi₂O₃·PbO is preferentially formed, followed by the compound 4Bi₂O₃·5PbO. The formation of the compound 4Bi₂O₃·6PbO was not confirmed while the formation of the compound Bi₂O₃ 3PbO occurs through a complex mechanism which includes an intermediate step in which a solid solution with the litharge structure was identified. Under isothermal conditions in the same temperature range the tendency to form the stoichiometric compounds increases. All compounds form, decompose and melt at temperatures between 530–780°C.