Preparation of TiO2-coated LiCo1/3Ni1/3Mn1/3O2 by electrostatic self-assembly method and its properties

A precursor of TiO₂–LiCo_1/3Ni_1/3Mn_1/3O₂ was prepared by electrostatic self-assembly method. The final product was obtained by heating the precursor at 400–450 °C for 4–6 h in air. X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), and electrochemical tests were used to examine the structural, morphology, elementary valence, and electrochemical characteristics. XRD indicated that the TiO₂-coated material can be indexed by α-NaFeO₂ layered structure, which belongs to hexagonal-type space group R3m. XPS results confirmed the existence of TiO₂ compound on the surface of the coated sample. The SEM image showed that the material had spherically porous morphology with the uniform size about 6 μm. The initial charge–discharge capacity of the TiO₂-coated LiCo_1/3Ni_1/3Mn_1/3O₂ material was 168.8/160.0 mAh/g. After 60 cycles, the discharge capacity of the TiO₂-coated LiCo_1/3Ni_1/3Mn_1/3O₂ sample was 147.0 mAh/g, and the coulombic efficiency was 94.0%. Compared with the uncoated sample, the electrochemical performance of TiO₂-coated LiCo_1/3Ni_1/3Mn_1/3O₂ was improved.