Effects of Al doping for Li[Li0.09Mn0.65*0.91Ni0.35*0.91]O2 cathode material

Li-rich Mn-based LiLi_0.09Mn_{0.65*(0.91???x)} Ni_{0.35*(0.91???x)} Al _x ]O₂ cathode materials have been prepared by traditional solid-state reaction. The lattice parameters a, c, and V have decreased, but c/a increased with the increase of Al doping. All the samples show analogy morphology of a quasi-spherical shape. LiLi_0.09Mn_0.591Ni_0.319]O₂ sample shows a higher initial discharge capacity of 239.4 mAh?g^?1 at 20 mA?g^?1, while LiLi_0.09Mn_0.582Ni_0.314Al_0.015]O₂ sample presents a higher discharge capacity of 170.1 mAh?g^?1 and ratio of 72.0 % with 200 vs. 20 mA?g^?1. The solid electrolyte interface resistance (R _SEI) and charge transfer process resistance (R _ct ) values are relatively smaller for Al-doped samples than those of non-doped samples. Almost no reduction is observed after 24-time cycles in different discharge rates for the samples prepared.