Temperature dependence of NO2 sensitivity of YSZ-based mixed potential type sensor attached with NiO sensing electrode

A mixed potential type yttria-stabilized zirconia-based sensor using NiO sensing electrode and Pt reference electrode was fabricated, and its NO₂ sensing characteristics were examined at various operating temperatures in the range of 700–950 °C. It was observed that the sensitivity to NO₂ strongly depends on the operating temperature of the sensor; the sensitivity decreases with increasing operating temperature, while the response/recovery rates increase. To rationalize this temperature dependence of NO₂ response, polarization curves and complex impedances of the sensor were measured in the base gas and in the sample gas (400 ppm NO₂?+?base gas) at various operating temperatures. It turned out that the operating temperature had a strong influence on the rate of anodic reaction of oxygen; the increased rate of anodic reaction leads to lower NO₂ sensitivity and quicker response/recovery at higher operating temperature.