Magnetic properties of RE0.7Ca0.3Mn0.95Fe0.05O3 (RE=Sm and Gd) manganites at low temperature

The magnetic properties of RE_0.7Ca_0.3Mn_0.95Fe_0.05O₃ perovskite with rare-earth cations (RE=Sm and Gd) were investigated by means of X-ray diffraction, Mössbauer spectroscopy, and low temperature (4.2-266 K) magnetization measurements. Structural characterization of these compounds shows that they both have orthorhombic (Pbnm) structure. The Mössbauer spectra show clear evidence of local structural distortion of the Mn(Fe)O₆ octahedron, which is based on the non-zero nuclear quadrupole interactions for high-spin Fe³⁺ ions. It was found that the local structural distortion increases significantly when Sm³⁺ is replaced by Gd³⁺. This distortion is attributed to the Jahn-Teller coupling strength as estimated from the Mössbauer effect results. The magnetic results indicate that the Curie temperature decreases as a result of replacing Sm by Gd. This is due to the decrease of the average A-site cationic radius 〈r_A〉. The rapid increase of magnetization at low temperature indicates the magnetic ordering of rare earth ions at the A-site.