Molecular weight distributions in radiation-induced polymerization. III. γ-Ray-induced polymerization of styrene at low temperatures

The kinetics of the γ-radiation-induced polymerization of styrene was studied at radiation intensities of 8 × 10⁴, 2.4 × 10⁵, 3.1 × 10⁵, and 8.3 × 10⁵ rad/hr over a temperature range of ?10°C to 30°C. The water content of the irradiated samples varied from 1.0 × 10^?3 to 7.5 × 10^?3 mole/l. The power dependence of the rate of polymerization on the dose rate at ?10°C varied from 0.53 to 0.71 as the water content of the sample varied from 7.5 × 10^?3 to 1.0 × 10^?3 mole/l. A value of 3.1 kcal/mole was determined for the overall activation energy. Molecular weight distribution studies by gel-permeation chromatography indicated the presence of two distinct peaks. The contribution of each peak was dependent on specific experimental parameters. Kinetic data and molecular weight distribution data indicate the coexistence of two propagating species. Analysis of the data strongly suggests that a free-radical mechanism and a cationic mechanism are involved.