Up-conversion emissions of Er3+-Yb3+ codoped Al2O3 nanoparticles by the arc discharge synthesis method

The Er³⁺-Yb³⁺ codoped Al₂O₃ nanoparticles with an average particle size of about 50 nm have been synthesized by an arc discharge synthesis method. The green and red up-conversion emissions centered at about 526, 547 and 677 nm, corresponding respectively to the ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 transitions of Er³⁺, were detected by a 978-nm semiconductor laser diode excitation. The Annealing has evident effect on the up-conversion emissions of the samples: The red up-conversion emission is noticeable before annealing; however, the green up-conversion emission becomes predominant after annealing. The mixture of (Er,Yb)₃Al₅O₁₂ and α-(Al,Er,Yb)₂O₃ phases is more favorable for green up-conversion emissions due to an enhancement of the ESA (I) of ⁴I_11/2+a photon→⁴F_7/2 and ET (III) of ²F_5/2(Yb³⁺)+⁴I_11/2(Er³⁺)→²F_7/2(Yb³⁺)+⁴F_7/2(Er³⁺) processes. The two-photon absorption up-conversion process is involved in the green and red up-conversion emissions. The results have proved that arc discharge synthesis is a new promising preparation technology for optical materials. Supported by National Natural Science Foundation of China (Grant No. 10804015), the Scientific Research Foundation for Doctor of Liaoning Province (Grant No. 20071095), and the Educational Committee Foundation of Liaoning Province (Grant No. 2008123)