Both the cubic and orthorhombic ZrW_0.8Mo_1.2O₈ were prepared by precursor-microwave route. The cubic phase belonged to β-ZrW₂O₈ structure type and the orthorhombic phase was refined with the structural model of LT- ZrMo₂O₈ by the Rietveld method. The orthorhombic phase belonged to Pmn2₁ space group and the cell parameters were a_o=0.597 1(9) nm, b_o=0.730 6(1) nm, c_o=0.912 7(1) nm, R_p%=9.37; wR_p%=11.81. The TEM images were also given. The comparison was made between precursor-heated and precursor-microwave routes. Metastable polymorphic phase was favorably formed by the latter method.

Microwave Synthesis and Characterization of Both Cubic and Orthorhombic ZrW0.8Mo1.2O8

Both the cubic and orthorhombic ZrW0.8Mo1.2O8 were prepared by precursor-microwave route. The cubic phase belonged to a-ZrW2O8 structure type and the orthorhombic phase was refined with the structural model of LT-ZrMo2O8 by the Rietveld method. The orthorhombic phase belonged to Pmn21 space group and the cell parameters were ao=0.597 1(9) nm, bo=0.730 6(1) nm, co=0.912 7(1) nm, Rp%=9.37; wRp%=11.81. The TEM images were also given. The comparison was made between precursor-heated and precursor-microwave routes. Metastable polymorphic phase was favorably formed by the latter method.